Daplen™ EH104AE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7kVgMt_Daplen-EH104AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EH104AE is a 12% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness, high melt flow rate and gives a good surface quality. Daplen EH104AE has been developed especially for the car industry to be used in automotive exterior parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 28.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1150 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 5.2 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, injection molding | 4.0 | kJ/m² | ISO 179/1eA |
| -20°C, injection molding | 5.5 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 31 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 30 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 5.5 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 33 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 47.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ISO 306/A |
| -- | 40.0 | °C | ISO 306/B |
| CLTE - Flow (-30 to 80°C) | 6.8E-5 | cm/cm/°C | Internal method |
| Melt Energy | 65.0 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 3.00 - 6.00 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FA70HH | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| Sylvin 6045E BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Buna® EP G 5567 | LANXESS Corporation | EPDM | Buna® EP |
| Hostacom X M2 T20/3 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| POLYblend PC/ABS 65 M10 | Polykemi AB | PC+ABS | POLYblend |