POLYNIL® P240 L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7iuxFg_POLYNIL-P240-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® P240 L is a high viscosity unreiforced Polyamide 66 (Nylon 66) for injection molding. This high molecular weight 5 viscosity Polyamide 66 resin is designed for improved wear resistance and melt strenght. POLYNIL® P240 L is FDA compliant. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.4 | % | |
| Flow : 23°C | 1.4 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | No Break | ||
| 30°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 72.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 750 | °C | |
| 3.20 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 3.20 mm | 750 | °C | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 980 | RTP Company | PSU | RTP |
| TRIREX® Compound 3025M10 | Samyang Corporation | PC | TRIREX® Compound |
| ACCUTECH™ CP0436W20L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Panlite® GN-3630H | TEIJIN LIMITED | PC | Panlite® |
| Plaslube® PA6/6 GF30 ML HS | Techmer Engineered Solutions | Nylon 66 | Plaslube® |