Telcar® TL-1446G
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7gtXe7_Telcar-TL-1446G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-1446G is a flame retardant thermoplastic elastomer designed for electrical applications requiring flexibility over a wide termperture range. Telcar TL-1446G is a high durometer grade that is RoHS compliant. This grade is UL listed and is suitable for both injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 3.5 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 2.0 | % | ASTM D955 |
| Transverse flow : 3.18mm | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 95 | ASTM D2240 | |
| Shaw D | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 3.05mm 2 | 7.93 | MPa | ASTM D412 |
| 300% strain, 3.05mm 3 | 9.48 | MPa | ASTM D412 |
| Tensile Strength (fracture, 3.05mm) | 14.5 | MPa | ASTM D412 |
| Tensile Elongation (fracture, 3.05mm) | 550 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (158°C, 168 hr) | -20 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (158°C, 168 hr) | -42 | % | ASTM D573 |
| Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil) | 2.0 | % | ASTM D471 |
| Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil) | 6.0 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -56.0 | °C | ASTM D746 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1 kHz) | 2.30 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.60 mm, All Colors) | V-0 | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | die cut from injection molded plaque |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| SuperLite® SL551600-100 (5.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Ferro PP TPP20AJ34NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Latilon 28D K/20 | LATI S.p.A. | PC | Latilon |
| Dryflex® SE 75A001 | ELASTO | TPE | Dryflex® |