Generic PSU
| Category: | PSU , Polysulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7gbzAY_Generic-PSU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PSU This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 1.23 - 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.69 - 0.80 | % | ASTM D955 |
| 23°C | 0.70 - 0.84 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 119 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2460 - 2830 | MPa | ASTM D638 |
| 23°C | 1800 - 2610 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 60.0 - 80.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 54.7 - 70.6 | MPa | ASTM D638 |
| 23°C | 58.4 - 76.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 5.0 - 75 | % | ASTM D638 |
| Fracture, 23°C | 73 - 75 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2250 - 2790 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 80.7 - 112 | MPa | ASTM D790 |
| Coefficient of Friction | 0.080 - 0.37 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 54 - 75 | J/m | ASTM D256 |
| 23°C | 5.0 - 7.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 370 - 2400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 178 - 183 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 173 - 174 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 168 - 180 | °C | ISO 75-2/A |
| CLTE - Flow | 5.6E-5 - 5.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+12 - 1.1E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 17 - 22 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.99 - 3.16 | ASTM D150 | |
| Dissipation Factor (23°C) | 7.0E-4 - 7.0E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 134 - 149 | °C | |
| Drying Time | 4.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.020 - 0.050 | % | |
| Rear Temperature | 331 - 332 | °C | |
| Middle Temperature | 330 - 344 | °C | |
| Front Temperature | 332 - 356 | °C | |
| Processing (Melt) Temp | 350 - 366 | °C | |
| Mold Temperature | 119 - 150 | °C | |
| Injection Pressure | 8.00 - 121 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PSUThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP1001SB | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Nymax™ 600 A Zip 43 Natural | PolyOne Corporation | Nylon 6 Alloy | Nymax™ |
| EPLAMID 66 CBR 15 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| TOTAL Polyethylene Lumicene® M 3423 UV black | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| Durez® 37006 | SBHPP | Phenolic | Durez® |