KRATON® G7720 GI-N
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | KRATON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7g6Tso_KRATON-G7720-GI-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Kraton G7720 GI-N is an easy processing, general purpose 57 Shore a hardness material designed for a wide variety of applications. It is supplied from North America in the physical forms identified below.
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 to 1.25 | g/cm³ | Internal Method |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | Internal Method | ||
| Shore A 1 | 62 | ||
| Shore A | 52 to 62 | ||
| Shore A, 10 sec | 57 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Flow | ASTM D412 | ||
| 100% Strain, 3.18 mm | 1.38 | MPa | |
| 300% Strain, 3.18 mm | 2.07 | MPa | |
| 500% Strain | 3.45 | MPa | |
| Tensile Strength - Flow (Yield, 3.18 mm) | 5.52 | MPa | ASTM D412 |
| Tensile Elongation - Flow (Break, 3.18 mm) | 700 | % | ASTM D412 |
| Tear Strength 2(3.18 mm) | 26.3 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 15 | % | |
| 70°C, 22 hr | 38 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 140 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | 130 | % | ASTM D573 |
| Change in Durometer Hardness (Shore A) | 2.0 | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -63.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3 | 51 | mm/min | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance 4(38°C) | No Cracking | ASTM D518/1149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Nozzle Temperature | 216 to 232 | °C | |
| Mold Temperature | 26.7 to 65.6 | °C | |
| Injection Pressure | 3.45 to 4.83 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.689 to 1.38 | MPa |
| Note Message | |
|---|---|
| 1 . | Instant |
| 2 . | Die C |
| 3 . | SAE J369 |
| 4 . | 100 pphm, 72 hr, 7X magnification |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cereplast Compostables® 2001 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| Larton K/20 | LATI S.p.A. | PPS | Larton |
| Iupilon® MB2213R | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |
| Sylvin 9067-65 Orange 593 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® TP 740-101 000000 | LANXESS GmbH | PBT+ASA | POCAN® |