TEKASTER™ F101M
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKASTER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7fCBWG_TEKASTER-F101M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKASTER™ F101M is a Polybutylene Terephthalate (PBT) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 120 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 70.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 153 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 210 to 260 | °C | |
| Front Temperature | 200 to 250 | °C | |
| Nozzle Temperature | 230 to 270 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 39.2 to 132 | MPa |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Visiloy™ 2650 | Technical Polymers, LLC | PC+PBT | Visiloy™ |
| LITAC-A® 100PCF | Nippon A&L Inc. | AS | LITAC-A® |
| Lupoy® GP2300 | LG Chem Ltd. | PC | Lupoy® |
| Luran® 2580 | Styrolution | SAN | Luran® |
| Plenco 04304 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |