INSTRUC PA610GF20
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7eP9dT_INSTRUC-PA610GF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Specific Volume | 0.820 | cm³/g | |
| Molding Shrinkage - Flow | 0.40 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 238 to 274 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-550S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| Vi-Chem PVC VNC95-80E-8804 | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| TYNEA 3530 | Tyne Plastics LLC. | Acetal (POM) Homopolymer | TYNEA |
| Fainplast PVC MPH 57 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hanwha Total PP HY301 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |