Order Products : sales@su-jiao.com
Elvaloy® AC 3117
| Category: | EnBA , Ethylene n-Butyl Acrylate Copolymer |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Elvaloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7eKoKw_Elvaloy-AC-3117.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Elvaloy® AC 3117 is a copolymer of ethylene and butyl acrylate. It is available in pellet form for use in conventional extrusion equipment designed to process polyethylene type resins. 17% Butyl Acrylate |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 60.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 99.0 | °C | ASTM D3418, ISO 3146 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Butyl Acrylate Content | 17.0 | wt% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C | |
| Cylinder Zone 5 Temp. | 185 | °C | |
| Adapter Temperature | 185 | °C | |
| Melt Temperature | 160 to 235 | °C | |
| Die Temperature | 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-636 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| XYRON™ X351V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NORYL™ N1150 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| ASTAMID™ MB3ZUV | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| EL-Lene™ M3804RW | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |