Lupolen 2420 K
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7dqigZ_Lupolen-2420-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lupolen 2420 K is a non-additivated, low density Polyethylene. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 11.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 0.6-1.6 mil (15-40 µ) | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 17.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 100 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 60 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 105 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy - Blown Film (50.0 µm) | 35.0 | J/cm | DIN 53373 |
| Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 170°C and a blow-up ratio of 1:2.5. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 651H | SABIC Americas, Inc. | PP Random Copolymer | SABIC® PP |
| BMC 945 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Chansieh Phenolic J-263-1 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Celstran® PA66-GF60-02-Natural | Celanese Corporation | Nylon 66 | Celstran® |
| COSMOPLENE® FY4012E | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |