TARODUR 100 X0
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TARODUR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7d5Kcq_TARODUR-100-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS self extinguishing UL94 V0, good mechanical, flow and surface finishing. UL94 V0 approuved @ 1,64 mm. UL746B approved. Available: all colors, heat stabilized (H). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.30 | % | ASTM D570, ISO 62 |
| Saturation | 0.70 | % | ASTM D570 |
| Saturation, 23°C | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 46.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 70.0 | MPa | ISO 178 |
| Yield | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 12 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 3 | 60.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525, ISO 306/A50 6 4 |
| -- | 90.0 | °C | ASTM D1525, ISO 306/B50 7 5 |
| Ball Pressure Test (75°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | > 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 70.0 to 80.0 | °C | |
| Pre-heater | 70.0 to 80.0 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fixmaster Conveyor Belt Repair | Loctite® | PUR, Unspecified | Fixmaster |
| Ebalta SG 2000 S / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Kumho EPS SEPS N30 | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| KOCETAL® GF302BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Sylvin 9925-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |