NAXELL™ PC100H
| Category: | PC , Polycarbonate |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXELL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7cYaL3_NAXELL-PC100H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PC100H is available in natural and opaque colors, Information and details are available upon request.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.18 mm) | 80 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 2280 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 3.18 mm) | 93.1 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 132 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 127 | °C | ASTM D648 |
| CLTE - Flow (-40 to 35°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 78.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 249 - 282 | °C | |
| Mold Temperature | 48.9 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 1.21 | MPa | |
| Screw Speed | 50 - 75 | rpm | |
| Cushion | 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 to 75% of injection pressureHold: 40 to 60% of injection pressureAir Flow Rate: 0.8-1.0 CFM per lb/hour resin processed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE HMW 1000950 | Amco Polymers | HDPE, HMW | PRIMATOP |
| NEXUS PE LLDPE-2020 Granular | Nexus Resin Group, LLC. | LLDPE | NEXUS PE |
| Hifax TRC 835P | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ THERMOCOMP™ RF006L compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ ZF006 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |