Megalon® 113GL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mega Polymers |
| Trademark: | Megalon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7bgiQy_Megalon-113GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Megalon® 113GL is a 13% glass fiber reinforced, nylon-6/6 offering an excellent balance of high temperature performance, dimensional stability, tensile strength and impact properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 4860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 241 | °C | ASTM D648 |
| Peak Melting Temperature | 263 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (lab tested only) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake LDPE EP413 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Abstron IM14GL | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Axiall PVC 3801 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Arylmax® P7000 | Polymics, Ltd. | PAEK | Arylmax® |
| K-Bin Rigid PVC KB-6108 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |