Jampilen RCXP598
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7bFSQU_Jampilen-RCXP598.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen RCXP598 is a medium modified random copolymer for the production of cast and blown films with reduced blooming effect. Jampilen RCXP598 is formulated with a general purpose stabilization package and does not contain any slip- or antiblocking agents. Jampilen RCXP598 offers easy processability on both cast and water-quenched blown film lines. The mechanical properties of films made with Jampilen RCXP598 are outstanding and the optical characteristics are superior to films made with conventional random copolymers. The seal initiation temperature is about 130°C and the blooming effect is minimal. Due to its good heat weldability, Jampilen RCXP598 is suitable for monolayer films as well as sealing layers in coextruded films or laminated structures (e.g. with BOPP, PA, polyester or aluminum). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 1 |
| Accelerated Oven Ageing (150°C) | 360 | hr | ASTM D3012 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 88 | ASTM D2457 | |
| Haze | 0.50 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SKYBOND® 8000 | Industrial Summit Technology Co. | API | SKYBOND® |
| Dynalloy™ OBC 8100-N50 | PolyOne Corporation | TPE | Dynalloy™ |
| Pearlbond™ 580 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlbond™ |
| SIBUR Synthetic Rubber NBR 3375 | SIBUR | NBR | SIBUR Synthetic Rubber |
| CYCOLAC™ INP338 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |