Kelon® B H CER/30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7b2VNR_Kelon-B-H-CER-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Mineral filler. Very high dimensional stability. Good elongation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 1.0 to 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4900 | MPa | |
| 60°C | 3000 | MPa | |
| 90°C | 1900 | MPa | |
| 120°C | 1600 | MPa | |
| 150°C | 1100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 80.0 | MPa | |
| Break, 60°C | 45.0 | MPa | |
| Break, 90°C | 35.0 | MPa | |
| Break, 120°C | 25.0 | MPa | |
| Break, 150°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 3.5 | % | |
| Break, 60°C | 4.5 | % | |
| Break, 90°C | 10 | % | |
| Break, 120°C | 20 | % | |
| Break, 150°C | 35 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® R37Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Latene® 7H2W-V0 | LATI S.p.A. | PP Homopolymer | Latene® |
| ISPLEN® PB 171 H1M | REPSOL | PP Impact Copolymer | ISPLEN® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| Delrin® FG500MP NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |