PRL NY6-GP2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7aKFXM_PRL-NY6-GP2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL NY6-GP2 is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 89.6 | MPa | |
| Break, 3.18 mm | 89.6 | MPa | |
| Flexural Modulus (3.18 mm) | 3100 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 191 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 73.9 | °C | |
| RTI Elec | UL 746 | ||
| 0.800 mm | 125 | °C | |
| 1.50 mm | 125 | °C | |
| 3.00 mm | 125 | °C | |
| 6.00 mm | 125 | °C | |
| RTI Imp | UL 746 | ||
| 0.800 mm | 65.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| 6.00 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 0.800 mm | 65.0 | °C | |
| 1.50 mm | 85.0 | °C | |
| 3.00 mm | 85.0 | °C | |
| 6.00 mm | 85.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.800 mm) | 30 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) (0.800 mm) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.800 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| 6.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) (0.800 mm) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.800 mm | PLC 4 | ||
| 1.50 mm | PLC 4 | ||
| 3.00 mm | PLC 3 | ||
| 6.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| 6.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 221 to 246 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 238 to 279 | °C | |
| Mold Temperature | 79.4 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 A TF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Shuang-Bang W-8157N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Andur AL 70 DP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Braskem PP R7051-10N | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |
| HANWHA EVA 2315 | Hanwha Chemical | EVA | HANWHA EVA |