InnoTuf® HP-2140A
| Category: | TSU-Ether , Polyurethane Thermoset Elastomer, Polyether Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7ZbrPT_InnoTuf-HP-2140A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-2140A is a high performance polyether based polyurethane elastomer formulated for hand-batch processing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or MDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.03 | g/cm³ | |
| Cured | 1.04 | g/cm³ | |
| Base Resin | 1.06 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 50 Mix Ratio by Weight: 47 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 300 to 420 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.13 | Pa·s | |
| 25°C 2 | 0.48 | Pa·s | |
| 25°C 3 | 0.63 | Pa·s | |
| Curing Time 4 | 29 | hr | |
| Gel Time | 20 to 30 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 35 to 45 | ASTM D2240 | |
| Tensile Strength | 4.14 | MPa | ASTM D638 |
| Tensile Elongation at Break | 480 | % | ASTM D638 |
| Tear Strength | 16.6 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 5 hours at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR WC 0521-48 R1 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| TRIREX® Compound TH3025N | Samyang Corporation | PC | TRIREX® Compound |
| Ultradur® B 4300 G6 LT BK15092 | BASF Corporation | PBT | Ultradur® |
| Huafon JF-W-AL6050 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 9995-68 Green 3215 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |