TATREN® HT 3 06
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Slovnaft Petrochemicals, s.r.o. |
| Trademark: | TATREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7YHhXk_TATREN-HT-3-06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TATREN HT 3 06 is homopolymer of good processing stability and it can be processed at high throughput. Additive package of this grade provides low water carry over during production of tapes. TATREN HT 3 06 is characterised by exceptionally high mechanical properties and high stiffness. Applications TATREN HT 3 06 is intended for production of high tenacity weaving tapes and monofilaments. It is well suitable to produce PP fabrics for big-bags production, carpet backing, ropes and marine ropes, twines etc. This grade can be used also for extrusion, sheet extrusion and thermoforming, injection moulding and compounding. TATREN HT 3 06 is suitable for food contact. The product complies with Food Contact Regulations. The grade is suitable for manufacturing of pharmaceutical packing-product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Injection Molded) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 9.0 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Injection Molded) | 6.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4807 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sanren Y3700C (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| DynaMix™ 2044-G | Polymer Dynamix | Nylon, Unspecified | DynaMix™ |
| Keliren® CM302 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Karina IVORY PVC COMPOUND -E 881-35/ 1-C-IS-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |