ACCUTECH™ HP0339M40CL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7YGLps_ACCUTECH-HP0339M40CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339M40CL is a polypropylene homopolymer (PP Homopoly) product, which contains 40% mica filler. It is available in North America. The main characteristics are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 51 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 33.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5800 | MPa | ASTM D790 |
| Flexural Strength | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 134 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 83.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 HI 25 GF BLK | RTP Company | Nylon 66 | RTP |
| SUSTARIN® H AF | Röchling Sustaplast SE & Co. KG | Acetal (POM) Homopolymer | SUSTARIN® |
| Badadur® PBT8 GF30 TM-Z2 | Bada AG | PBT | Badadur® |
| BJB Polyurethane TC-886 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Karina WHITE PVC COMPOUND -E 807-10/203-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |