PRIME TPO E-2710
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | PRIME TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7WBnwO_PRIME-TPO-E-2710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIME TPO E-2710 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 12.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain (Break) | < 500 | % | ISO 527-2 |
| Flexural Modulus | 240 | MPa | ISO 178 |
| Flexural Stress | 11.5 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Modulus | JIS Z1702 | ||
| MD : 80 µm | 280 | MPa | |
| TD : 80 µm | 280 | MPa | |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 80 µm | 33.0 | MPa | |
| TD : Break, 80 µm | 33.0 | MPa | |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 80 µm | < 500 | % | |
| TD : Break, 80 µm | < 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80.0 µm 1 | 0.60 | % | |
| 80.0 µm 2 | 13 | % |
| Note Message | |
|---|---|
| 1 . | Internal |
| 2 . | All |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC GW 3042 NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| apirex® MBL 25 H | API SpA | TPU-Polyether | apirex® |
| Kepital® TE-23(FU2015) | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| INNOBATCH® PPH 3160 | Inno-Comp Ltd. | PP Homopolymer | INNOBATCH® |
| Formolene® 6145O | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |