Miramid® TE30CW
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Uk7WH_Miramid-TE30CW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding grade, glass fibre-reinforced, heat stabilized, technical parts for use under the bonnet |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.36 | g/cm³ | ISO 1183 |
| -- | 1360 | kg/m³ | ISO 1183 1 |
| Viscosity Number | |||
| 96% H2SO4 (Sulphuric Acid) | 130 | cm³/g | ISO 307 |
| -- | 130 | cm³/g | ISO 307, 1157, 1628 2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 220 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 9000 | MPa | ISO 527-2 |
| -- | 9000 | MPa | ISO 527-2 3 |
| Tensile Stress | |||
| Break, 23°C | 175 | MPa | ISO 527-2 |
| Break | 175 | MPa | ISO 527-2 4 |
| Tensile Strain | |||
| Break, 23°C | 3.0 | % | ISO 527-2 |
| Break | 3.0 | % | ISO 527-2 5 |
| Flexural Stress (23°C) | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 12.0 | kJ/m² | ISO 179/1eA 6 |
| Charpy Unnotched Impact Strength | |||
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 70.0 | kJ/m² | ISO 179/1eU 7 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Burning Behav. at thickness h (1.50 mm) | HB | ISO 1210 8 | |
| Glow Wire Flammability Index (1.00 mm) | 650 | °C | IEC 60695-2-12 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 280 to 300 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ SX 218 V50 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Sindustris PC GP5201 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| NOVADURAN® 5010GN6-30M8X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Chemlon® 60MGF6 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Fenochem C 4800 | Chemiplastica, Inc. | Phenolic | Fenochem |