WONDERLOY® PC-540
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | WONDERLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7TSGdd_WONDERLOY-PC-540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WONDERLOY® PC-540 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 23.5 | cm³/10min | ISO 1133 |
| Spiral Flow | 11.2 | cm | Internal Method |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 58.8 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/50 |
| Break | 53.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break, 23°C | 100 | % | ASTM D638 |
| Break | 95 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 23°C | 2460 | MPa | ASTM D790 |
| -- 1 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 89.2 | MPa | ASTM D790 |
| -- 2 | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 640 | J/m | ASTM D256 |
| -- | 43 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 3 | 92.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ASTM D1525 4 |
| -- | 106 | °C | ISO 306/A50 |
| -- | 99.0 | °C | ISO 306/B50 |
| CLTE - Flow (40 to 100°C) | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/hr |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1200 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| STAR-THERM® E T-3C | EPIC Polymers | PBT | STAR-THERM® |
| Cheng Yu A705G3 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| ELIX™ Ultra 4105 | ELIX Polymers, S. L. | PC+ABS | ELIX™ Ultra |
| Orgalloy® LE 60XV | Arkema | Nylon 6 Alloy | Orgalloy® |