Generic LCP - Glass\Mineral
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7TKXUv_Generic-LCP---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.66 - 1.68 | g/cm³ | ASTM D792 |
| 23°C | 1.65 - 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.010 - 0.20 | % | ASTM D955 |
| 23°C | 0.0 - 0.51 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11900 - 14200 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 110 - 131 | MPa | ISO 527-2 |
| 23°C | 110 - 142 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 - 1.6 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 11500 - 13000 | MPa | ASTM D790 |
| 23°C | 10600 - 14100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 130 - 181 | MPa | ASTM D790 |
| 23°C | 130 - 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 - 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 270 - 335 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 230 - 270 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 235 - 261 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.0E-6 - 9.2E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.3E-5 - 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 - 2.1E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 21 - 48 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C) | 3.70 - 4.35 | IEC 60250 | |
| Dissipation Factor (23°C) | 9.7E-3 - 0.030 | IEC 60250 | |
| Arc Resistance | 181 - 183 | sec | ASTM D495 |
| Comparative Tracking Index | 150 - 200 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 160 | °C | |
| Drying Time | 3.0 - 6.1 | hr | |
| Rear Temperature | 320 - 360 | °C | |
| Middle Temperature | 325 - 365 | °C | |
| Front Temperature | 340 - 365 | °C | |
| Nozzle Temperature | 335 - 365 | °C | |
| Processing (Melt) Temp | 335 - 366 | °C | |
| Mold Temperature | 95.0 - 105 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V955 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| McCann PP M20TCPP20 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Sindustris PBT SG3251M | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| NYCOA Polyamide 1838 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| Kumho SBR 1769 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |