TOTAL Polyethylene MDPE HL 323
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Sf2yI_TOTAL-Polyethylene-MDPE-HL-323.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene HL 323 is a Medium Density Polyethylene material. It is available in North America for coextrusion or extrusion. Important attributes of TOTAL Polyethylene HL 323 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.23 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882A | ||
| 1% Secant, MD : 25 µm, Blown Film | 441 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 586 | MPa | |
| Tensile Strength | ASTM D882A | ||
| MD : Yield, 25 µm, Blown Film | 12.4 | MPa | |
| TD : Yield, 25 µm, Blown Film | 19.3 | MPa | |
| MD : Break, 25 µm, Blown Film | 57.2 | MPa | |
| TD : Break, 25 µm, Blown Film | 36.5 | MPa | |
| Tensile Elongation | ASTM D882A | ||
| MD : Break, 25 µm, Blown Film | 500 | % | |
| TD : Break, 25 µm, Blown Film | 900 | % | |
| Dart Drop Impact (25 µm, Blown Film) | < 50 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 18 | g | |
| TD : 25 µm, Blown Film | 1400 | g | |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 12 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 126 | °C | ASTM D3417 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 216 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-70910U | Spartech Polycom | PC | Spartech |
| T-Blend® 9203B-F80I-X | TSRC Corporation | SEBS | T-Blend® |
| Tuffak® T | Altuglas International of Arkema Inc. | PC | Tuffak® |
| Grilon® BM 16 nat | EMS-GRIVORY | Nylon, Unspecified | Grilon® |
| SABIC® EPDM 245 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |