LEXAN™ OQ3820 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7SYWNc_LEXAN-OQ3820-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Viscosity, UV-stabilized grade for ophthalmic lenses. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.4 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.32 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Break 3 | 72.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.3 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 130 | % | ASTM D638 |
| Break | 140 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2410 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 94.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 14 | J/m | ASTM D256 |
| 23°C | 920 | J/m | ASTM D256 |
| -30°C 11 | 12 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 85.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 126 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 15 |
| -- | 143 | °C | ISO 306/B50 |
| -- | 144 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 120*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 MF PRTA011 PR305 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Yuyao PBT 6158 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| Ethylplus CO 125 | Fainplast Compounds S.r.l | PE, Unspecified | Ethylplus |
| OmniCarb™ PC/ABS GR10 | OMNI Plastics, LLC | PC+ABS | OmniCarb™ |
| TECACOMP® PA66 CF15 black 4058 | Ensinger GmbH | Nylon 66 | TECACOMP® |