Comco PA 6 G GK 30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Comco-Plastic GmbH |
| Trademark: | Comco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7S2K0H_Comco-PA-6-G-GK-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Comco PA 6 G GK 30 is a Polyamide 6 (Nylon 6) material filled with 30% glass bead. It is available in Europe. Primary attribute of Comco PA 6 G GK 30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Shore Hardness (Shore D) | 85 | -- | ISO 868 | |
| Ball Indentation Hardness | 250 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 100 | 100 | MPa | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | > 4.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 225 | -- | °C | |
| CLTE - Flow | ||||
| 23 to 60°C | 8.0E-5 | -- | cm/cm/°C | |
| 23 to 100°C | 9.0E-5 | -- | cm/cm/°C | |
| Thermal Conductivity | 0.30 | -- | W/m/K | |
| Maximum Service Temperature | ||||
| in air continuosly | 110 | -- | °C | |
| in air for short periods | 170 | -- | °C | |
| Service Temperature - Minimum | -40 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D black nuclear | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| Sumikon® PM-6432 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| VYLOPET® EMC341 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| BONDYRAM® 1001CN | Polyram Ram-On Industries | PP Copolymer | BONDYRAM® |
| Lucon® PO6062 | LG Chem Ltd. | PPE+PS | Lucon® |