Lumiloy® TX5002
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7RzVBr_Lumiloy-TX5002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, High Flow PPO/PA Alloy Description High Flow, High Heat Resistance Application Electric and Electronic parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (285°C/5.0 kg) | 68 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 62.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 3.20 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 160 | J/m | |
| 23°C, 3.20 mm | 210 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 186 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Suggested Max Moisture | > 0.050 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 285 to 325 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTATRON PPS MOD | Röchling Sustaplast SE & Co. KG | PPS | SUSTATRON |
| Crastin® SK645FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Fiberfil® PP-60/V2 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| LNP™ STAT-KON™ KEP33 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Lusin® Clean LD 250 | Chem-Trend L.P. | Unspecified | Lusin® |