Zytel® ST811HS NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7R0Mei_ZytelST811HSNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super Toughened, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 0.90 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 6.8 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 900 | 400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 31.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 29 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | -- | % | ISO 527-2 |
| Flexural Modulus | 850 | 360 | MPa | ISO 178 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 4.0 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 71 | 130 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 25.0 | -- | J | ISO 6603-2 |
| 23°C | 16.0 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 47.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 50.0 | 0.00 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 95.0 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 2.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.8E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 31 | -- | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 8.0E-3 | 0.055 | IEC 60250 | |
| 1 MHz | 0.014 | 0.18 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.75 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2600 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | -- | W/m/K |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.880 | -- | g/cm³ | |
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM TR-305 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| Baydur® 646 (20 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| ESENTTIA 30R40CD | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Petrothene® GA605034X02 | LyondellBasell Industries | LLDPE | Petrothene® |
| OTECH TPE OTE7030 - Power Jacket | OTECH Corporation | TPE | OTECH TPE |