LNP™ LUBRICOMP™ RFL36L compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7R09H4_LNP-LUBRICOMP-RFL36L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. Also known as: LNP* LUBRICOMP* Compound RFL-4036 LE Product reorder name: RFL36L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 to 1.5 | % | ASTM D955 |
| Across Flow : 24 hr | 1.4 | % | ISO 294-4 |
| Flow : 24 hr | 0.53 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 10100 | MPa | ISO 527-2/1 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 152 | MPa | |
| Break | 152 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 2.8 | % | |
| Break | 2.8 | % | |
| Flexural Modulus | |||
| -- | 8270 | MPa | ASTM D790 |
| -- | 9300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 214 | MPa | ASTM D790 |
| -- | 230 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.67 | ||
| vs. Itself - Static | 0.65 | ||
| Wear Factor - Washer | 4.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 61 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.6 | J | ASTM D3763 |
| -- | 2.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 260 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 247 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene 2220 | Resirene, S.A. de C.V. | PS (MIPS) | Resirene |
| SureSpec RP-350C | Genesis Polymers | PP Random Copolymer | SureSpec |
| CP PRYME® Polyethylene PE100LLD-50M | Chase Plastics Services Inc. | LLDPE | CP PRYME® Polyethylene |
| Hostaform® C 9021 TF XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Kepex® 3300M | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |