SCHULADUR® A GF 30 HIR SCHWARZ
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7QSkUC_SCHULADUR-A-GF-30-HIR-SCHWARZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced, hydrolysis stabilized PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 127 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 7800 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 203 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ISO 306/A50 |
| -- | 205 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 40 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 750 | °C | IEC 60695-2-12 |
| 3.00 mm | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P UT-100 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Tislamid® PA66 PA66 20 GBR | Tisan | Nylon 66 | Tislamid® PA66 |
| LAPEROS® GA473 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| EVALENE® PP PRB0202 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |
| Sylvin 9266-70 Blue 8417 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |