SABIC® PPcompound 9510E
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7PqgNW_SABIC-PPcompound-9510E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 9510E is a mineral filled modified polypropylene for automotive interior applications. This material combines high stiffness, good impact, low emissions and good processing. SABIC® PPcompound 9510E is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.75 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 20.4 | MPa | |
| Break, 3.20 mm, Injection Molded | 13.6 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 21 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.5 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.0E-5 | cm/cm/°C | |
| 23 to 80°C | 8.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTM® 85S | Cytec Industries Inc. | Phenolic | MTM® |
| ULTEM™ STM1500 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| AKROMID® B3 GF 50 black (2939) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Karina GREEN PVC COMPOUND -E 898-40/ 71-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8270-82FU White 1227 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |