SCHULINK® XL 351
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | SCHULINK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7PgMIE_SCHULINK-XL-351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SCHULINK® XL 351 is a Crosslinked Polyethylene product. It can be processed by rotational molding and is available in North America. Primary characteristic: crosslinkable. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.942 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Rotational Molded) | 19.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Rotational Molded) | 500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Rotational Molded) | 689 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (-40°C, 3.18 mm, Rotational Molded) | 81 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Rotational Molded) | 62.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH300J8 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| DINALON® PA 6.6 | Grupo Repol | Nylon 66 | DINALON® |
| Durethan® BKV 35 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Keyflex® BT 1155D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| KRYSTALFLEX™ PE192 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |