Order Products : sales@su-jiao.com
4TECH® 9KY22130
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Pdy6z_4TECH-9KY22130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9KY22130 is a Prime Standard Flow 30% Glass Fibre Reinforced PBT / ASA Blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 210 | °C | ISO 75-2/B |
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 50.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9962-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tislamid® PA66 PA66 25 GBR | Tisan | Nylon 66 | Tislamid® PA66 |
| Adflex KS021P | LyondellBasell Industries | TPO (POE) | Adflex |
| Karina COMP. PVC CRYSTAL -E 85/253-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |