KumhoSunny PC/ABS HAC8260H
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7PRO5y_KumhoSunny-PC-ABS-HAC8260H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAC8260H is high flow PC/ABS resin. HAC8260H has an excellent low temperature resistance properties. HAC8260H is mainly used in mobile phone housing,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 106 | °C | ASTM D648 |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PE 8425 | Ponachem Compound GmbH | HDPE | PONACOM PE |
| Shuang-Bang C-8157N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Calsak ABS CS-72L | Calsak Polymers | ABS | Calsak ABS |
| EMERGE™ PC 4330-10 | Trinseo | PC | EMERGE™ |
| Sylvin 9950-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |