ULTRACLEAR is a series of water clear casting resins with excellent physical properties, such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 40.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ASTM D638 |
| Tensile Strength | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 1340 | MPa | ASTM D790 |
| Flexural Strength | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 73.0 | °C | |
| 1.8 MPa, Unannealed | 59.0 | °C |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 600 | cP | ASTM D4878 |
| Demold Time (21°C) | 1400 | min | Internal Method |
| Post Cure Time (70°C) | 8.0 to 16 | hr |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ GZK3200 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| ADDINYL C2 V30 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| ALCOM® PA66 910/1 GF30 PTFE20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| AZDEL™ C467-B01 | Azdel, Inc. | PP, Unspecified | AZDEL™ |
| Sylvin 8692-74 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |