LNP™ LUBRICOMP™ RN001S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7NDk7a_LNPLUBRICOMPRN001Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lubricated Polyamide 66 injection moulding resin. Also known as: LNP* LUBRICOMP* Compound RL4210S1 Product reorder name: RN001S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.6 - 2.0 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 8.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 92.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 3300 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | > 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | ISO 180/1A |
| -20°C | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 230 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 90.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 252 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS F5330 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| ExxonMobil™ HDPE HD 6714.17 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| KRATON® G7723 GS-N | Kraton Polymers LLC | SEBS | KRATON® |
| OxyVinyls庐 220F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| CABELEC® CC6135 | Cabot Corporation | PS (GPPS) | CABELEC® |