Sindustris ABS LLG814W
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7MkVEA_Sindustris-ABS-LLG814W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LLG814W is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LLG814W are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 45.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 25 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 98 | J/m | |
| -30°C, 6.40 mm | 88 | J/m | |
| 23°C, 3.20 mm | 250 | J/m | |
| 23°C, 6.40 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 101 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 92.0 | °C | |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 30 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 68.6 to 88.3 | MPa | |
| Screw Speed | < 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J708UG | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Keliren® CPE1135C | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| OP - PC - Filled PC B15-7SS | Oxford Polymers | PC | OP - PC - Filled |
| Sylvin 9048-97 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LG ABS AF365 | LG Chem Ltd. | ABS | LG ABS |