PLUSTEK PB350M6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7KRRbG_PLUSTEK-PB350M6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLUSTEK PB350M6 is a polyamide 6 (nylon 6) material, which contains a 30% mineral filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of the PLUSTEK PB350M6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.80 - 1.1 | % | ASTM D955 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 6.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Continuous Use Temperature | 70.0 | °C | ASTM D794 |
| Melting Temperature (DSC) | 218 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 100 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Density, ISO 1183, was tested in accordance with DIN 53479.The value listed as Water absorbtion, ISO 62, was tested in accordance with DIN 53495.The value listed as HDT A (1.8 Mpa), ISO 75A, was tested in accordance with DIN 53461.The value listed as HDT B (0.45 Mpa), ISO 75B, was tested in accordance with DIN 53461.The value listed as Surface Resistivity, IEC 60093, was tested in accordance with DIN 53482.The value listed as Volume Resistivity, IEC 60093, was tested in accordance with DIN 53482.The value listed as Dielectric Strength, ASTM D149, was tested in accordance with VDE 0303/4.The value listed as Moisture Absorbtion 23°C/50%RH, ISO 62, was tested in accordance with DIN 53714.Max Temp. Short Peaks Operation: 180 °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3890H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Exceed™ 3518CB | ExxonMobil Chemical | mPE | Exceed™ |
| MAJORIS BT200 | AD majoris | PP, Unspecified | MAJORIS |
| Pearlbond™ 520 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| EPALINE 786A34 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPALINE |