tefabloc® TP SD 333 70A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | tefabloc® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7IX7lf_tefabloc-TP-SD-333-70A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
tefabloc®TP SD 333 70A is a thermoplastic elastomer (TPE) material,. This product is available in North America or Europe. The processing method is injection molding. tefabloc®The main features of TP SD 333 70A are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.80 | % | Internal method |
| Flow direction | 1.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec, Injection Molded) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion | 280 | mm³ | DIN 53516 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Resistance to Aging | 110 | °C |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -50 - 100 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Color Fastness | ISO 105-A02 | ||
| -- 1 | 4/5 | ISO 105-A02 | |
| 100 hr | 5 | ISO 105-A02 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 20% strain | 2.00 | MPa | ISO 37 |
| 100% strain | 2.50 | MPa | ISO 37 |
| Tensile Stress (Break) | 3.80 | MPa | ISO 37 |
| Tensile Elongation (Break) | 590 | % | ISO 37 |
| Tear Strength 2 | 28 | kN/m | ISO 34-1 |
| Compression Set 3 | ISO 815 | ||
| 23°C, 22 hr | 22 | % | ISO 815 |
| 50°C, 22 hr 4 | 27 | % | ISO 815 |
| 50°C, 22 hr 5 | 41 | % | ISO 815 |
| 70°C, 22 hr 6 | 40 | % | ISO 815 |
| 70°C, 22 hr 7 | 50 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 180 | °C | |
| Injection Rate | Moderate | ||
| Screw Compression Ratio | 2.5:1.0 - 3.0:1.0 |
| Injection instructions |
|---|
| Screw Speed: Medium |
| Note Message | |
|---|---|
| 1 . | 1000 hr |
| 2 . | Method B, right-angle specimen (without cut) |
| 3 . | Type B |
| 4 . | relaxation 50°C |
| 5 . | relaxation 23°C |
| 6 . | relaxation 70°C |
| 7 . | relaxation 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4560 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SAXAMID™ 226F7 | SAX Polymers | Nylon 66 | SAXAMID™ |
| Sylvin 9053-50 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| PEXTIN™ PET 545 BK | Pier One Polymers, Inc. | PET | PEXTIN™ |
| ADLAS® O07FJB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADLAS® |