Lumid® GP3200A(W)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7IVdGK_Lumid-GP3200A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumid® GP3200A(W) is a Polyamide 6 (Nylon 6) material filled with 20% mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Lumid® GP3200A(W): Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.80 to 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4310 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 130 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 4.00 | ASTM D150 | |
| Arc Resistance 5 | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 230 to 255 | °C | |
| Middle Temperature | 245 to 260 | °C | |
| Front Temperature | 245 to 270 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| Teflon® PTFE 605XT X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Braskem PP D180A2 | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Arnitel® EM460 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| MAJORIS G357 | AD majoris | PP, Unspecified | MAJORIS |