Horda E8575-A1
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7HKrPE_Horda-E8575-A1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
E8575-A1 is a crosslinkable, strippable semi-conductive compound, designed for XLPE insulated cables and use in both dry and steam curing processes. E8575-A1 is recommended for Italian, French and Spanish standards on XLPE. Specifications E8575-A1 meets the requirements as below, when optimal processing extrusion and end testing procedure are used: AEIC- CS 8 (latest edition) BS 6622 IECA: 60502 NF C 33-223 NEMA WC 7-1996/ICEA S-95-658 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 20 | MU | ISO 289 |
| Moisture 1 | ppm |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset 2(200°C) | 36 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Stripping Force - XLPE 3(23°C) | 1.4 - 1.6 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -10 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | -40 | % | ASTM D573 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 3.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Hopper Temperature | 23.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 110 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP CP350WV | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Cri-Line NPC-820 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| DJSilicone NE-271 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Escorene™ Ultra LD 730.09 Molding | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| ESPOLEX WT501 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |