Infino SA-1100
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7GuOz8_InfinoSA1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino SA-1100 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.46 - 0.56 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.48 - 0.58 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.48 - 0.58 | % | ISO 2577 |
| Traffic : 3.20mm | 0.46 - 0.56 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 66.0 | MPa | ASTM D638 |
| Fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 91 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 70 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 690 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 200 | J/m | ASTM D256 |
| 23°C 10 | 70 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 to 3.0mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (1.5 mm) | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Hot air dryer | 110 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 4.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.030 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 280 - 285 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Injection Pressure | 68.6 - 206 | MPa | |
| Back Pressure | 0.490 | MPa | |
| Screw Speed | 30 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 280°CHot Runner Valve Nozzle Temperature: 280°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Impax 450 with VANISH | Primex Plastics Corporation | PS (GPPS) | Prime Impax |
| SCHULABLEND® (PA/PP) M/MO | A. Schulman Europe | Nylon+PP | SCHULABLEND® |
| BITONER® TR-120 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| ANYPOL SE-1600P | SH Energy & Chemical | PS (EPS) | ANYPOL |
| LubriOne™ LB3300-5002 RS BK | PolyOne Corporation | PBT | LubriOne™ |