Iupilon® ELV2020
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7GquMq_IupilonELV2020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wear Resistance Improved |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.30 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Lateral flow : 3.20mm | 0.50 - 0.70 | % | |
| Traffic : 3.20mm | 0.50 - 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.12 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 53.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.6 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 142 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 126 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Mold Temperature | 70 - 100 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE XT10B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| HANWHA CLBA-8924BK | Hanwha Chemical | LDPE | HANWHA |
| Jam HDPE HF4750 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Karina CLEAR PVC COMPOUND -E 80/321-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PD120BK11 | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |