RTP 3485-4

Category: LCP , Liquid Crystal Polymer
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 7Ge5BO_RTP-3485-4.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Carbon Fiber
General Information
Filler / Reinforcement
  • Carbon fiber reinforced material, 30% filler by weight
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.51g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.050%ASTM D955
Water Absorption (23°C, 24 hr)0.10%ASTM D570
MechanicalNominal ValueUnitTest Method
Tensile Modulus 31000MPaASTM D638
Tensile Strength 117MPaASTM D638
Tensile Elongation (Yield)0.80%ASTM D638
Flexural Modulus 24800MPaASTM D790
Flexural Strength 190MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)75J/mASTM D256
Unnotched Izod Impact (3.20 mm)320J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)318°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)V-0UL 94
Additional InformationNominal ValueUnit
Primary Additive 30%
InjectionNominal ValueUnit
Drying Temperature 149°C
Drying Time 8.0hr
Dew Point -28.9°C
Processing (Melt) Temp 363 - 399°C
Mold Temperature 65.6 - 93.3°C
Injection Pressure 68.9 - 124MPa
Injection instructions
The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position.
Resin Grade Manufacturer Category Trademark
ResMart Ultra MB Black ResMart LLDPE ResMart Ultra
Shandong PA1010 PA1010 Shandong Dongchen Engineering Plastics Co., Ltd. Nylon 1010 Shandong PA1010
BCC Resins BC 5105 BCC Products Inc. Epoxy BCC Resins
Bynel® 42E703 DuPont Packaging & Industrial Polymers LDPE Bynel®
REV Materials 8003-002 REV Materials PP, Unspecified REV Materials