PLUSTEK RB133
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7GZIfX_PLUSTEK-RB133.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INDUSTRIAL GRADE GENERAL PURPOSE POLYAMIDE 6 FOR INJECTION MOULDING APPLICATIONS. RB703 IS A UV STABILIZED GRADE. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.4 - 1.8 | % | ASTM D955 |
| -- | 1.4 - 1.8 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | > 70.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | > 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | > 95.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | > 60 | J/m | ASTM D256 |
| 23°C | > 7.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | > 160 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | > 65.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 218 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 10 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene LDPE 1022 FH 24 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| NEFTEKHIM PS 535 | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Hylon® N1200THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LNP™ THERMOCOMP™ AX04518 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| Durez® 37081 | SBHPP | Phenolic | Durez® |