ASTALOY™ PC/ABS M150-28328
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7FlDcL_ASTALOY-PC-ABS-M150-28328.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS M150-28328 is highly pigmented, ultra high heat resistance and ultra high impact strength alloy of Polycarbonate/ABS and is designed for moulding applications requiring reduced light bleed and exceptional impact toughness, product rigidity, ultra high heat resistance whilst maintaining mouldability. Typical applications include light box display units Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS M150U-28328 ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 54.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 130 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 550 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 55.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 121 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 126 | °C | |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 265 to 285 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V955 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Axiall PVC 7450 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LNP™ THERMOCOMP™ RB004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Daelim Po1y® EP2501 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |