Order Products : sales@su-jiao.com

INEOS LDPE 20N430

Category:	LDPE , Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7FhiWh_INEOSLDPE20N430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Additive free LDPE homopolymer extrusion coating, injection moulding and compounding product

Benefits & Features
20N430 special polymer structure gives the following properties:

For extrusion coating:

Well balanced Neck In and Draw Down performance

Good adhesion performance and sealing properties

For injection moulding and compounding:

Excellent flexibility

Good transparency

Absence of any kind of additive allowing tailor formulation of specific compounds and master-batches

Applications
Extrusion coating and laminating grade designed for a medium to high coating line speed.

20N430 is also suitable for injection moulding of flexible products (caps and closures, food containers, soft tubes, technical parts) as well as for the production of compounds.

General Information
Features	Low density Homopolymer Good flexibility Good adhesion No additive
Uses	Laminate Composite Pipe fittings Shield Masterbatch Food container Coating application Shell
RoHS Compliance	Contact manufacturer
Appearance	Clear/transparent
Forms	Particle
Processing Method	Lamination method Composite Extrusion coating Injection molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.921	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	8.5	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, Compression Molded)	44		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C, Injection Molded)	170	MPa	ISO 527-2/1BA/1
Tensile Stress			ISO 527-2/50
Yield, 23°C, molded	11.0	MPa	ISO 527-2/50
Fracture, 23°C, compression molding	10.0	MPa	ISO 527-2/50
Tensile Strain (Break, 23°C, Compression Molded)	600	%	ISO 527-2/50

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	87.0	°C	ISO 306/A50
Melting Temperature ¹	108	°C	ISO 11357-3

Injection	Nominal Value	Unit
Processing (Melt) Temp	190 - 250	°C

Extrusion	Nominal Value	Unit
Melt Temperature	280 - 325	°C

Note Message
1 .	DSC 2nd heating 10°C/min

Resin Grade	Manufacturer	Category	Trademark
Akulon® Ultraflow K-FG3	DSM Engineering Plastics	Nylon 6	Akulon® Ultraflow
CP PRYME® Nylon 6 N213L	Chase Plastics Services Inc.	Nylon 6	CP PRYME® Nylon 6
Daelim Po1y® PH-470	DAELIM INDUSTRIAL CO., LTD.	PP Homopolymer	Daelim Po1y®
Expandable PS RF23W	INEOS Styrenics International SA	PS (EPS)	Expandable PS
Fiberfil® PP-60/TC/20/FD	Fiberfil® Engineered Plastics Inc.	PP Homopolymer	Fiberfil®