LEXAN™ HP1REU resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Fd7w2_LEXAN-HP1REU-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO sterilizable. Contains mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 28 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2370 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 3 | 65.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 640 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 121 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 140 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 120*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Apec® 1895 | Covestro - Polycarbonates | PC | Apec® |
| Clariant Nylon 6/6 PA-111 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ColorFast® FRA204 | LTL Color Compounders, Inc. | ABS | ColorFast® |
| HIPLEX® HXM 45060 | HIP-PetroHemija | HDPE | HIPLEX® |
| KumhoSunny ABS 760 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |