Plexiglas® Satinice df23 7N

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7FOgg9_Plexiglas-Satinice-df23-7N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PLEXIGLAS® Satinice df23 7N, based on PLEXIGLAS® 7N, is characterized by diffuse scattering of light.

Typical properties of PLEXIGLAS® molding compound are

good flow

high mechanical strength, surface hardness and mar resistance

very good weather resistance.

Special properties of PLEXIGLAS® Satinice df23 7N are

excellent lightdiffusion combined with excellent light transmission.

Application:
Used for injection molding items for lighting engineering applications

Examples:
applications that call for good light diffusion combined with optimum transmission

General Information
Features	Good Flow Good Weather Resistance High Hardness High Strength Light Stabilized
Uses	Lighting Diffusers
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	4.10	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3400	MPa	ISO 527-2/1
Tensile Stress (Break)	65.0	MPa	ISO 527-2/5
Tensile Strain (Break)	2.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.8	kJ/m²	ISO 179/1
Charpy Unnotched Impact Strength (23°C)	17	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	101	°C	ISO 75-2/B
1.8 MPa, Unannealed	97.0	°C	ISO 75-2/A
Glass Transition Temperature	108	°C	ISO 11357-2
Vicat Softening Temperature	105	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	6.3E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	700	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Additional Information	Nominal Value	Unit	Test Method
Half-Value Angle	21.0	°	DIN 5036

Optical	Nominal Value	Unit	Test Method
Transmittance ¹	81.0	%	ISO 13468-2

Extrusion	Nominal Value	Unit
Drying Temperature	> 95.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	220 to 260	°C
Die Temperature	220 to 260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Shandong PA612 A5G6301	Shandong Dongchen Engineering Plastics Co., Ltd.	Nylon 612	Shandong PA612
Telcar® TELC-1000-92	Teknor Apex Company	TPE	Telcar®
Sylvin 86022-85 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Mylar® S (92 guage)	DuPont Teijin Films U.S.	PET	Mylar®
NYCOA Polyamide 2012	Nycoa (Nylon Corporation of America)	Nylon+TPE	NYCOA Polyamide