Plasti-Paste® Trowelable
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Plasti-Paste® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7F7pe3_Plasti-Paste-Trowelable.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plasti-Paste® is a two component fiber resin that is designed for vertical surface application. Part A is a liquid and Part B is a paste. Mix ratio is 1A : 3B by volume (41A:100B by weight). It has no odor and pot life is 8 - 10 minutes depending on mass. Demold time (can be handled) is about 90 minutes depending on mass. Plasti-Paste® holds a vertical surface without sagging and cures to a strong, durable and lightweight plastic. Suitable as a mother mold / support shell (reinforces shape of rubber mold during casting), or as a laminating material. Can be pigmented with So-Strong® color tints from Smooth-On. Add cabosil or other filler as an extender or for special effects. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.863 | cm³/g | ASTM D1475 |
| Viscosity | Paste | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 41A:100B by weight 1A:3B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.50 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1160 | MPa | ASTM D638 |
| Tensile Strength (Break) | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 23.5 | MPa | ASTM D790 |
| Compressive Modulus | 336 | MPa | ASTM D695 |
| Compressive Strength | 23.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 54.4 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 8.0 to 10 | min | ASTM D2471 |
| Demold Time (23°C) | 90 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4051 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Menzolit® SMC 0150 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Flontech® FT-BRR40-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| INNOPOL® PP CS 1-3820 | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Sylvin 9067-80 Grey 9469 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |