Generic Nylon 12 - Glass Fiber
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7F5DU6_Generic-Nylon-12---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 12 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 - 1.38 | g/cm³ | ASTM D792 |
| 23°C | 1.11 - 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.41 | % | ASTM D955 |
| 23°C | 0.10 - 0.71 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.091 - 0.60 | % | ASTM D570 |
| 23°C, 24 hr | 0.10 - 0.41 | % | ISO 62 |
| Saturated, 23°C | 0.40 - 1.2 | % | ASTM D570 |
| Saturated, 23°C | 0.80 - 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.39 - 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 5880 - 16100 | MPa | ASTM D638 |
| 23°C | 3910 - 19200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 85.4 - 130 | MPa | ASTM D638 |
| Yield, 23°C | 99.1 - 130 | MPa | ISO 527-2 |
| Fracture, 23°C | 106 - 151 | MPa | ASTM D638 |
| Fracture, 23°C | 63.8 - 191 | MPa | ISO 527-2 |
| 23°C | 92.9 - 108 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.8 - 10 | % | ASTM D638 |
| Yield, 23°C | 1.5 - 7.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.8 - 11 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 7.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3720 - 9050 | MPa | ASTM D790 |
| 23°C | 11.0 - 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 93.6 - 244 | MPa | ASTM D790 |
| 23°C | 96.0 - 213 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 - 26 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 47 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 85 - 260 | J/m | ASTM D256 |
| 23°C | 1.8 - 18 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 570 - 1400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 176 - 178 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 169 - 178 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 160 - 174 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 - 176 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 80.0 - 160 | °C | ISO 75-2/C |
| Continuous Use Temperature | 104 - 151 | °C | ASTM D794 |
| Vicat Softening Temperature | 170 - 175 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 174 - 185 | °C | |
| -- | 178 | °C | ISO 11357-3, ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 8.0E-6 - 4.9E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-5 - 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.9E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+2 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 18 - 44 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.75 | IEC 60250 | |
| Comparative Tracking Index | 595 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.9 - 105 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.030 - 0.50 | % | |
| Rear Temperature | 220 - 258 | °C | |
| Middle Temperature | 226 - 268 | °C | |
| Front Temperature | 231 - 266 | °C | |
| Processing (Melt) Temp | 232 - 266 | °C | |
| Mold Temperature | 51.6 - 90.0 | °C | |
| Injection Pressure | 64.2 - 87.5 | MPa | |
| Holding Pressure | 39.0 - 52.5 | MPa | |
| Back Pressure | 0.252 - 0.525 | MPa | |
| Screw Speed | 45 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 12 - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP380S | PolyMirae | PP Copolymer | Moplen |
| CompaDur® 151 natural (001) | DimeLika Plast GmbH | PBT | CompaDur® |
| DENIFORM 2510 | Vamp Tech | Acetal (POM) Copolymer | DENIFORM |
| Echo® RPC30G BK | Ravago Manufacturing Americas, LLC | PP Homopolymer | Echo® |
| Kuraray Poval® PVA 420H | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |